Enhanced thermal shrinkage behavior of phenolic-derived carbon aerogel-reinforced by HNTs with superior compressive strength performance

A novel carbon/m-HNTs composite aerogel was synthesized by introducing the modified halloysite nanotubes (m-HNTs) into phenolic (PR) aerogels through chemical grafting, followed with carbonization treatment. In order to explore the best proportion of HNTs to phenolic, the micromorphology of PR/m-HNTs were investigated by SEM before carbonization, confirming 10 wt% of m-HNTs is most beneficial to the porous network of aerogels. The interaction between PR and HNTs was studied by FTIR spectra, and microstructure evolution of the target product-carbon/m-HNTs composite aerogel were illustrated by SEM and TEM techniques. SEM patterns indicated that the carbon/m-HNTs aerogels maintain a stable porous structure at 1000 °C (carbonization temperature), while a ~20 nm carbon layer was formed around m-HNTs generating an integral unit through TEM analysis. Specific surface area and pore size distribution of composite aerogels were analyzed based on mercury intrusion porosimetry and N₂ adsorption–desorption method, the obtained results stayed around 500 m²g^?1 and 1.00 cm³g^?1 (pore volume) without significant discrepancy, compared with pure aerogel, showing the uniformity of pore size. The weight loss rate (26.76%) decreased greatly compared with pure aerogel, at the same time, the best volumetric shrinkage rate was only 30.83%, contributed by the existence of HNTs supporting the neighbor structure to avoid over-shrinking. The highest compressive strength reached to 4.43 MPa, while the data of pure aerogel was only 1.52 MPa, demonstrating the excellent mechanical property of carbon/m-HNTs aerogels.     

50型螺旋式钢板仓卷边设备理论分析与试验

结合已有卷边设备的生产工艺和特点,研发了国内首台50型螺旋式钢板仓卷边设备,并完成了4次样机调试试验.分析了新型卷边设备关键机构的工作原理,对下轧辊调节机构进行了力学计算分析,完成了卷边孔型设计.利用显示动力学软件数值模拟了5 mm钢板的冷弯成形(卷边)过程,分析了成形过程中的等效应力和等效塑性应变.通过4次样机调试试验,将调试结果与模拟结果对比.结果 表明,折弯5 mm钢板比折弯3 mm的钢板力载荷大很多,有必要研发新型的卷边设备;卷边设备的后3个工位的应力峰值比前3个工位大,其中工位6应力峰值最大;文中的卷边孔型设计合理;卷边过程的模拟结果与试验结果一致.     

深竖井大吨位提升机高比压高摩擦因数衬垫的研制

针对深竖井、大吨位的提升条件下,摩擦衬垫需要高比压和高摩擦因数的难题,在工况分析和参数设计的基础上,研制了比压为2.5 MPa、摩擦因数为0.28的摩擦衬垫,并分别对衬垫的稳定性、抗比压能力、硬度特性、压力特性和磨损情况进行试验.委托第三方检测验证,衬垫的比压试验值达到9.8 MPa,摩擦因数试验值达到0.381,满足实验室的指标要求.     

液滴撞击干燥倾斜壁面铺展实验研究

通过高速摄影技术及像素分析方法对液滴撞击干燥倾斜壁面进行实验研究，分析了不同倾斜角及韦伯数（We）对液滴飞溅及铺展的影响，结果表明，倾斜角的增加有利于抑制飞溅的产生；We一定时，液滴的前铺展因子随着倾斜角的增加而增加，后铺展因子随着倾斜角的增加而减小；液滴的前后初始铺展速度均大于液滴的撞击速度，且随着倾斜角的增加而减小。      

刮板输送机中板仿生耐磨优化试验研究

刮板输送机中板磨损失效已成为输送机运行故障的主要原因之一，为了提高中板耐磨性，基于蜣螂非光滑单元进行了仿生中板设计，以磨损量为响应值，进行了单因素和响应面法优化试验。根据响应面法试验结果得到的因素显著性影响顺序（从高至低）依次为：径向距离，深径比，直径，节距角。基于试验结果建立了磨损量与因素的回归预测模型，经试验对比发现，预测模型与真实试验的相对误差为3.2%。在特定工况（煤散料粒度为6~8 mm、载荷为20 N、刮板链速为0.65 m/s及试验时长为6 600 s）下，当深径比为1.41、直径为0.69 mm、节距角为6.55°和径向距离为4.66 mm时，磨损量最小，仿生中板的耐磨性提高了12.6%。分析其耐磨机理发现，与光滑板相比，仿生板的磨粒磨损及黏着磨损较轻。凹坑分布可破坏持续切削中板表面的煤粒运动状态。中板的仿生优化可为今后刮板输送机的设计提供一定参考。     

川北某黑色页岩型铼矿工艺矿物学研究

通过矿相显微镜、扫描电镜、电子探针、X射线能谱元素面分析等多种手段综合研究了川北某黑色页岩型铼矿中铼的赋存状态。样品为黑色页岩,有机碳含量较高。粘土矿物总量为14.6%,黄铁矿含量16.2%,石英含量37.7%。样品具典型的粘土结构,矿物粒度微细。铼有两种赋存状态,一种呈类质同象形式赋存于黄铁矿内,另一种则以分散形式存在。典型黄铁矿测点Re平均含量为0.024%。黄铁矿是Re的重要载体矿物。建议通过浮选分离黄铁矿,从而实现Re的富集。